Potassium fluotitanate manufacture and device background

ABSTRACT

The invention provides a Potassium Fluotitanate (K 2 TIF6) manufacture process. The Potassium Fluotitanate (K 2 TIF6) manufacture process includes steps: A. providing titanium ferrum powder to a reaction furnace and adding HF and peroxide solution to react with the titanium ferrum powder sufficiently to manufacture H 2 TiF 6 , B. filtrating the sufficiently mixed solution of step A and adding it to another reaction furnace, and then after the H 2 TiF 6  cools off, adding Potassium Chloride (KCl) solution to react with the mixed solution to manufacture Potassium Fluotitanate (K 2 TiF 6 ); C. adding K 2 CO 3  solution to the remaining solution of step B and react with the remaining solution and controlling the pH value, the element Fe is recycled by a form of Fe(OH) 3  flocculent precipitate and the Potassium Chloride (KCl) and KF solution are recycled. This invention has these advantages: adding peroxide to the titanium ferrum powder can oxidize Fe 2+  into Fe 3+  and adding K 2 CO 3  solution to clean element Fe out by a form of Fe(OH) 3  flocculent precipitate, and the hydrofluoric acid (HF) can be recycled which can realize the HF zero polluting discharge.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention belongs to the fine chemical industry, especially to a Potassium Fluotitanate (K₂TiF₆) manufacture process and device.

2. Description of the Related Art

The Potassium Fluotitanate (K₂TiF₆) is used to be one of the basic material of manufacturing Al—Ti—B alloy, so its quantity and purity may affect the manufacture of the Al—Ti—B alloy. According to the manufacture of Potassium Fluotitanate (K₂TiF₆), for some traditional process, such as using H₂TiF₆, or H₂TiO₃, a lot of heat may be generated when the titanium ferrum powder is mixed so that the temperature of the reaction furnace may rise to 100˜200° C. This will lead to generate a lot of hydrofluoric acid (HF) steam. Meanwhile, a lot of waste including element fluorine may be generated to be a solution to environment. According to the traditional Potassium Fluotitanate (K₂TiF₆) manufacture process, the solution by the hydrofluoric acid (HF) and element Fe is a serious problem.

SUMMARY OF THE INVENTION

The present invention is directed to provide a Potassium Fluotitanate (K₂TiF₆) manufacture process which can reduce the generation of waste residue and liquid including Element Fluorine by adding K₂CO₃ solution.

According to this invention, a Potassium Fluotitanate (K₂TIF₆) manufacture process comprises following steps:

A. providing titanium ferrum powder to a reaction furnace and adding HF and peroxide solution to react with the titanium ferrum powder sufficiently to manufacture H₂TiF₆;

B. filtrating the sufficiently mixed solution of step A and adding it to another reaction furnace, and then after the H₂TiF₆ cools off, adding Potassium Chloride (KCl) solution to react with the mixed solution to manufacture Potassium Fluotitanate (K₂TiF₆), the Potassium Fluotitanate (K₂TiF₆) is recycled by centrifuge dripping filtrating; and

C. adding K₂CO₃ solution to the remaining solution of step B and react with the remaining solution and controlling the pH value, the element Fe is recycled by a form of Fe(OH)₃ flocculent precipitate and the Potassium Chloride (KCl) and KF solution are recycled.

What is preferred is the peroxide is inorganic peroxide or organic peroxide.

What is preferred is the inorganic peroxide is H₂O₂ or K₂O₂, and the organic peroxide is CH₃CO₂OH.

What is preferred is during the step C, the pH value is in a range of 2˜3, 3˜4, 4˜5, or 5˜7.

The present invention is directed to provide a Potassium Fluotitanate (K₂TiF₆) manufacture device to ensure the reaction and recycle the HF stream.

What is preferred is A Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace comprising a reaction furnace main body, a sealing cover sealed the reaction furnace main body, an output, and a stirring unit 12 disposed in the reaction furnace main body, wherein the sealing cover comprises several hole accesses to add hydrofluoric acid (HF), titanium ferrum powder accesses, and HF steam recycling condensation device.

What is preferred is wherein the HF steam recycling condensation device including several bent condenser tubes, an HF recycling groove is disposed at the end of the bent part, the condenser tube further comprises a condensation water device connecting to the adjacent condenser tube.

What is preferred is The Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace according to claim 6, wherein the hydrofluoric acid (HF) steam recycling condensation device comprises bent condenser tube and an air blower is disposed at the bent part of the condenser tube separately.

What is preferred is the Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace according to claim 7, wherein a graphite layer is disposed at the inside of the reaction furnace main body and the material of the stirring unit is PolyVinyl Chloride (PVC) or Polypropylene (PP).

This invention has these advantages: adding peroxide to the titanium ferrum powder can oxidize Fe²⁺ into Fe³⁺ and adding K₂CO₃ solution to clean element Fe out by a form of Fe(OH)₃ flocculent precipitate, and the hydrofluoric acid (HF) can be recycled which can realize the HF zero polluting discharge. And meanwhile, the Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace can recycle the HF stream and oxidize Fe²⁺ into Fe³⁺ and adding K₂CO₃ solution to clean element Fe out by a form of Fe(OH)₃ flocculent precipitate.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other features and advantages of the various embodiments disclosed herein will be better understood with respect to the following description and drawings, in which like numbers refer to like parts throughout, and in which:

FIG. 1 is a cross-sectional schematic view of a Potassium Fluotitanate manufacturing reaction furnace according to an embodiment of present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS Example 1

As shown in FIG. 1, a Potassium Fluotitanate (K2TIF6) manufacturing reaction furnace is provided. The Potassium Fluotitanate (K2TIF6) manufacturing reaction furnace includes a reaction furnace main body 10, a sealing cover sealed the reaction furnace main body, an output 15, and a stirring unit 12 disposed in the reaction furnace main body. The sealing cover includes several hole accesses 11 to add hydrofluoric acid (HF), titanium ferrum powder accesses 13, and HF steam recycling condensation device including several bent condenser tubes 14. An air blower 143 is disposed at the bent part of the condenser tube separately, and an HF recycling groove 142 is disposed at the end of the bent part. The condenser tube further includes a condensation water device 143 connecting to the adjacent condenser tube. An HF recycle device 144 is disposed at the end of the condenser tube to recycle HF which can realize the HF zero polluting discharge. A graphite layer is disposed at the inside of the reaction furnace main body. The material of the stirring unit is PolyVinyl Chloride (PVC) or Polypropylene (PP) to sufficiently mix the titanium ferrum powder with a low cost.

A Potassium Fluotitanate (K₂TiF₆) manufacturing process includes following steps:

A. providing titanium ferrum powder to a reaction furnace and adding HF and hydrogen peroxide to react with the titanium ferrum powder sufficiently to manufacture H₂TiF₆:

According to this embodiment, the quantity of the titanium ferrum powder is one ton. The concentration of the HF is in a range of 5˜20% and the quantity is about 2.5 tons. The concentration of the hydrogen peroxide is in a range of 5˜30%, what is preferred is 10˜20% and quantity is about 3 tons. Adding 10˜20% hydrogen peroxide to the HF can oxidize Fe²⁺ into Fe³⁺ of the titanium ferrum powder in order to avoid generating FeTiF₆. Thus, the element Fe can be cleaned out by a form of Fe(OH)₃ flocculent precipitate in the following steps.

B. filtrating the sufficiently mixed solution of step A and adding it to another reaction furnace, and then after the H₂TiF₆ cools off, adding Potassium Chloride (KCl) solution with a concentration 30˜35% to react with the mixed solution to manufacture Potassium Fluotitanate (K₂TiF₆):

H₂TiF₆+KCl→K₂TIF₆↓+HCl,

According to this embodiment, the quantity of the Potassium Chloride (KCl) is three tons.

The Potassium Fluotitanate (K₂TiF₆) is recycled by centrifuge dripping filtrating and the remaining solution is transmitted to a third reaction furnace.

C. adding K₂CO₃ solution with a concentration 30˜35% to the remaining solution of step B and react with the remaining solution.

H₃FeF₆+K₂CO₃+HCl+H₂O→Fe(OH)₃↓+KCl+KF+H₂O,

The quantity of the K₂CO₃ solution is two tons and its pH value is in a range of 3˜4. The element Fe is recycled by a form of Fe(OH)₃ flocculent precipitate and the Potassium Chloride (KCl) and KF solution are recycled to be reused.

Example 2

A Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace is provided. The Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace includes a reaction furnace main body 10, a sealing cover sealed the reaction furnace main body, an output 15, and a stirring unit 12 disposed in the reaction furnace main body. The sealing cover includes several hole accesses 11 to add hydrofluoric acid (HF), titanium ferrum powder accesses 13, and HF steam recycling condensation device including several bent condenser tubes 14. An air blower 143 is disposed at the bent part of the condenser tube separately, and an HF recycling groove 142 is disposed at the end of the bent part. The condenser tube further includes a condensation water device 143 connecting to the adjacent condenser tube. An HF recycle device 144 is disposed at the end of the condenser tube to recycle HF which can realize the HF zero polluting discharge. A graphite layer is disposed at the inside of the reaction furnace main body. The material of the stirring unit is PolyVinyl Chloride (PVC) or Polypropylene (PP) to sufficiently mix the titanium ferrum powder with a low cost.

A Potassium Fluotitanate (K₂TiF₆) manufacturing process includes following steps:

A. providing titanium ferrum powder to a reaction furnace and adding HF and hydrogen peroxide to react with the titanium ferrum powder sufficiently to manufacture H₂TiF₆:

According to this embodiment, the quantity of the titanium ferrum powder is one ton. The concentration of the HF is in a range of 5˜20% and the quantity is about 2.5 tons. The concentration of the peracetic acid is in a range of 5˜30%, what is preferred is 10˜20% and quantity is about 3 tons. Adding 10˜20% hydrogen peroxide to the HF can oxidize Fe²⁺ into Fe³⁺ of the titanium ferrum powder in order to avoid generating FeTiF₆. Thus, the element Fe can be cleaned out by a form of Fe(OH)₃ flocculent precipitate in the following steps.

B. filtrating the sufficiently mixed solution of step A and adding it to another reaction furnace, and then after the H₂TiF₆ cools off, adding Potassium Chloride (KCl) solution with a concentration 15˜20% to react with the mixed solution to manufacture Potassium Fluotitanate (K₂TiF₆):

H₂TiF₆+KCl→K₂TiF₆↓+HCl,

According to this embodiment, the quantity of the Potassium Chloride (KCl) is three tons.

The Potassium Fluotitanate (K₂TiF₆) is recycled by centrifuge dripping filtrating and the remaining solution is transmitted to a third reaction furnace.

C. adding K₂CO₃ solution with a concentration 15˜20% to the remaining solution of step B and react with the remaining solution.

H₃FeF₆+K₂CO₃+HCl+H₂O→Fe(OH)₃↓+KCl+KF+H₂O,

The quantity of the K₂CO₃ solution is two tons and its pH value is in a range of 4˜5. The element Fe is recycled by a form of Fe(OH)₃ flocculent precipitate and the Potassium Chloride (KCl) and KF solution are recycled to be reused. 

What is claimed is:
 1. A Potassium Fluotitanate (K₂TIF₆) manufacture process comprises following steps: A. providing titanium ferrum powder to a reaction furnace and adding HF and peroxide solution to react with the titanium ferrum powder sufficiently to manufacture H₂TiF₆:

B. filtrating the sufficiently mixed solution of step A and adding it to another reaction furnace, and then after the H₂TiF₆ cools off, adding Potassium Chloride (KCl) solution to react with the mixed solution to manufacture Potassium Fluotitanate (K₂TiF₆): H₂TiF6+KCl→K2TIF6↓+HCl, the Potassium Fluotitanate (K₂TiF₆) is recycled by centrifuge dripping filtrating; and C. adding K₂CO₃ solution to the remaining solution of step B and react with the remaining solution and controlling the pH value, H₃FeF₆+K₂CO₃+HCl+H₂O→Fe(OH)₃↓+KCl+KF+H₂O, the element Fe is recycled by a form of Fe(OH)₃ flocculent precipitate and the Potassium Chloride (KCl) and KF solution are recycled.
 2. The Potassium Fluotitanate (K₂TiF₆) manufacture process according to claim 1, wherein the peroxide is inorganic peroxide or organic peroxide.
 3. The Potassium Fluotitanate (K₂TiF₆) manufacture process according to claim 1, wherein the inorganic peroxide is H₂O₂ or K₂O₂, and the organic peroxide is CH₃CO₂OH.
 4. The Potassium Fluotitanate (K₂TiF₆) manufacture process according to any claim of claim 1 to claim 3, wherein during the step C, the pH value is in a range of 2˜3, 3˜4, 4˜5, or 5˜7.
 5. A Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace comprising a reaction furnace main body, a sealing cover sealed the reaction furnace main body, an output, and a stirring unit disposed in the reaction furnace main body, wherein the sealing cover comprises several hole accesses to add hydrofluoric acid (HF), titanium ferrum powder accesses, and HF steam recycling condensation device.
 6. The Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace according to claim 5, wherein the HF steam recycling condensation device including several bent condenser tubes, an HF recycling groove is disposed at the end of the bent part, the condenser tube further comprises a condensation water device connecting to the adjacent condenser tube.
 7. The Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace according to claim 6, wherein the hydrofluoric acid (HF) steam recycling condensation device comprises bent condenser tube and an air blower is disposed at the bent part of the condenser tube separately.
 8. The Potassium Fluotitanate (K₂TIF₆) manufacturing reaction furnace according to claim 7, wherein a graphite layer is disposed at the inside of the reaction furnace main body and the material of the stirring unit is PolyVinyl Chloride (PVC) or Polypropylene (PP). 